Eparency Original All-Purpose Resin
Can be used to cast anything, from small jewellery to deep casting river tables. each pour should not exceed 20mm depth for river table size, and not exceed 50mm depth for smaller casting such as pyramids etc. It can also be used for coating, however not suitable for making beach scenes coating, waves, cells or other effects due to its low viscosity nature. Small items would cure slower (approx. 3 days) and bigger items would cure slightly faster. If intending to have a fast curing process Eparency fast curing resin would be more suitable.
100% Australian owned and Australian manufactured
Directions
Mix resin and hardener in exactly 2:1 ratio by volume ( 2 parts A and 1 part B) Using a plastic or silicone container for mixing and mix thoroughly, scrape sides and bottom of container to fully integrate products. Please use a mixing container that is clean and free of contamination. Tiny contamination would deteriorate the quality of final result. Do not use metal, especially aluminium containers to mix or mixtures will turn milky colour. Once the product is poured into the mould, let the resin settle allowing air bubbles or foam to float to the surface, most bubbles will float to the surface and burst themselves. Any remaining bubbles or foam can be removed with a heat gun or Blow torch.
Specifications
- Mixing quantity (the more you mix, the fast it cures and vice versa)
- Mixing ratio: 2:1 (2 Parts A and 1 Part B)
- Application temperature: Wide temperature range through summer to winter (higher room temperature will speed up the curing).
- Pot life: 2-4 hours (Data based on 100ml mixing; 20 degree C room temperature). Please pour this product into mould as soon as possible, to avoid bubbling.
- Time to reach non-tacky: 10-30 hrs Depending on the room temperature (Data based on 100ml mixing)
- Time to reach full cure: 48 hrs (Data based on 100ml mixing)
- Viscosity: 600 cps for Part A (Brookfield 20 rpm) 450 cps for Part B (Brookfield 20 rpm)
- Clarity: Pt-Co value < 10 for both Part A and Part B
- Compatibility: Binding to metal, inorganic materials including cement; stone, natural materials including wood; particle board, most plastics except polyethylene, polypropylene, EPDM.